Carbon-Carbon Composite (3D structure)

(submitted by the website administration)

Carbon-Carbon Composite (3D structure)
Composition: carbon matrix + 3D oriented carbon fibers
Property Value in metric unit Value in US unit
Density 1.8 *10³ kg/m³ 112 lb/ft³
Flexural strength
(Z direction)
96 MPa 13900 psi
Flexural strength
(X-Y direction)
38 MPa 5500 psi
Compressive strength
(Z direction)
96 MPa 13900 psi
Compressive strength
(X-Y direction)
73 MPa 10600 psi
Tensile strength
(Z direction)
79 MPa 11500 psi
Tensile strength
(X-Y direction)
25 MPa 3600 psi
Modulus of elasticity
(Z direction)
89 GPa 12900 ksi
Modulus of elasticity
(X-Y direction)
25 GPa 3600 ksi
Flexural modulus of elasticity
(Z direction)
19 GPa 2800 ksi
Flexural modulus of elasticity
(X-Y direction)
5.7 GPa 830 ksi
Thermal conductivity
(200ºC, Z direction)
148 W/(m*K) 1026 BTU*in/(hr*ft²*ºF)
Thermal conductivity
(200ºC, X-Y direction)
130 W/(m*K) 901 BTU*in/(hr*ft²*ºF)
Specific heat capacity, 200ºC 1338 J/(kg*K) 0.32 BTU/(lb*ºF)