Wrought copper alloy C61000 (Aluminum Bronze)

(submitted by the website administration)

Wrought copper alloy C61000 (Aluminum Bronze)
Chemical composition: Al=8.0%, Cu=balance
Property Value in metric unit Value in US unit
Density 7.78 *10³ kg/m³ 486 lb/ft³
Modulus of elasticity 117 GPa 17000 ksi
Thermal expansion (20 ºC) 17.8*10-6 ºCˉ¹ 9.9*10-6 in/(in* ºF)
Specific heat capacity 377 J/(kg*K) 0.090 BTU/(lb*ºF)
Thermal conductivity 69.2 W/(m*K) 480 BTU*in/(hr*ft²*ºF)
Electric resistivity 11.5*10-8 Ohm*m 11.5*10-6 Ohm*cm
Tensile strength (annealed) 359 MPa 52000 psi
Yield strength (annealed) 117 MPa 17000 psi
Elongation (annealed) 45 % 45 %
Hardness (annealed) 60 RB 60 RB
Tensile strength (cold work) 414 MPa 60000 psi
Yield strength (cold work) 186 MPa 27000 psi
Elongation (cold work) 30 % 30 %
Hardness (cold work) 85 RB 85 RB
Annealing temperature 600-700 ºC 1110-1300 ºF
Liquidus temperature 1041 ºC 1905 ºF
Solidus temperature 1030 ºC 1890 ºF