Wrought copper alloy C15000 (Zirconium Copper)

(submitted by the website administration)

Wrought copper alloy C15000 (Zirconium Copper)
Chemical composition: Zr=0.15%, Cu = 99.8% min
Property Value in metric unit Value in US unit
Density 8.89 *10³ kg/m³ 555 lb/ft³
Modulus of elasticity 129 GPa 18700 ksi
Thermal expansion (20 ºC) 16.9*10-6 ºCˉ¹ 9.4*10-6 in/(in* ºF)
Specific heat capacity 394 J/(kg*K) 0.092 BTU/(lb*ºF)
Thermal conductivity 367 W/(m*K) 2544 BTU*in/(hr*ft²*ºF)
Electric resistivity 1.86*10-8 Ohm*m 1.86*10-6 Ohm*cm
Tensile strength (annealed) 255 MPa 37000 psi
Yield strength (annealed) 76 MPa 11000 psi
Elongation (annealed) 50 % 50 %
Hardness (annealed) 40 RF 40 RF
Tensile strength (cold work) 365 MPa 53000 psi
Yield strength (cold work) 338 MPa 49000 psi
Elongation (cold work) 23 % 23 %
Hardness (cold work) 90 RF 90 RF
Annealing temperature 425-650 ºC 800-1200 ºF
Liquidus temperature 1080 ºC 1976 ºF
Solidus temperature 980 ºC 1796 ºF

Related internal links

Related external links

wrought_copper_alloy_c15000_zirconium_copper.txt · Last modified: 2012/06/02 by dmitri_kopeliovich
Promote in SubsTech       Creative Commons License Except where otherwise noted, this work is licensed under a Creative Commons Attribution-Noncommercial-Share Alike 3.0 License