Wrought copper alloy C63000 (Aluminum Bronze)

(submitted by the website administration)

Wrought copper alloy C63000 (Aluminum Bronze)
Chemical composition: Al=10.0%, Fe=3.0%, Ni=5%, Cu=balance
Property Value in metric unit Value in US unit
Density 7.58 *10³ kg/m³ 473 lb/ft³
Modulus of elasticity 121 GPa 17500 ksi
Thermal expansion (20 ºC) 16.2*10-6 ºCˉ¹ 9.0*10-6 in/(in* ºF)
Specific heat capacity 377 J/(kg*K) 0.090 BTU/(lb*ºF)
Thermal conductivity 39.1 W/(m*K) 271 BTU*in/(hr*ft²*ºF)
Electric resistivity 19.3*10-8 Ohm*m 19.3*10-6 Ohm*cm
Tensile strength (as fabricat.) 689 MPa 100000 psi
Yield strength (as fabricated) 414 MPa 60000 psi
Elongation (as fabricated) 15 % 15 %
Shear strength (as fabricated) 427 MPa 62000 psi
Fatigue strength (as fabricat.) 248 MPa 36000 psi
Hardness (as fabricated) 96 RB 96 RB
Tensile strength (cold.work+ann.) 814 MPa 118000 psi
Yield strength (cold work+ann.) 517 MPa 75000 psi
Elongation (cold work+anneal) 15 % 15 %
Shear strength (cold work+ann.) 483 MPa 70000 psi
Fatigue strength (cold work+ann.) 255 MPa 37000 psi
Hardness (cold work+anneal) 98 RB 98 RB
Annealing temperature 650-815 ºC 1200-1500 ºF
Liquidus temperature 1054 ºC 1930 ºF
Solidus temperature 1035 ºC 1895 ºF