Wrought aluminum alloy 1060

(submitted by the website administration)

Wrought aluminum alloy 1060
Chemical composition: Si=0.25%, Fe=0.35%, Al = 99.6% min
Property Value in metric unit Value in US unit
Density 2.705 *10³ kg/m³ 169 lb/ft³
Modulus of elasticity 69 GPa 10000 ksi
Thermal expansion (20 ºC) 23.6*10-6 ºCˉ¹ 13.1*10-6 in/(in* ºF)
Specific heat capacity 900 J/(kg*K) 0.215 BTU/(lb*ºF)
Thermal conductivity 231 W/(m*K) 1600 BTU*in/(hr*ft²*ºF)
Electric resistivity 2.81*10-8 Ohm*m 2.81*10-6 Ohm*cm
Tensile strength (annealed) 69 MPa 10000 psi
Yield strength (annealed) 28 MPa 4000 psi
Elongation (annealed) 43 % 43 %
Shear strength (annealed) 48 MPa 7000 psi
Fatigue strength (annealed) 21 MPa 3000 psi
Hardness (annealed) 19 HB 19 HB
Tensile strength (H16) 110 MPa 16000 psi
Yield strength (H16) 103 MPa 15000 psi
Elongation (H16) 8 % 8 %
Shear strength (H16) 69 MPa 10000 psi
Fatigue strength (H16) 45 MPa 6500 psi
Hardness (H16) 30 HB 30 HB
Annealing temperature 343 ºC 650 ºF