Wrought aluminum-magnesium-silicon alloy 6201

(submitted by the website administration)

Wrought aluminum-magnesium-silicon alloy 6201
Chemical composition: Si=0.7%, Mg=0.8%, B=0.06% max. Al balance
Property Value in metric unit Value in US unit
Density 2.69 *10³ kg/m³ 168 lb/ft³
Modulus of elasticity 69 GPa 10000 ksi
Thermal expansion (20 ºC) 23.4*10-6 ºCˉ¹ 13.0*10-6 in/(in* ºF)
Specific heat capacity 895 J/(kg*K) 0.214 BTU/(lb*ºF)
Thermal conductivity 205 W/(m*K) 1420 BTU*in/(hr*ft²*ºF)
Electric resistivity 3.16*10-8 Ohm*m 3.16*10-6 Ohm*cm
Tensile strength (T81) 330 MPa 47900 psi
Yield strength (T81) 310 MPa 45000 psi
Elongation (T81) 6 % 6 %
Shear strength (T81) 200 MPa 29000 psi
Fatigue strength (T81) 105 MPa 15200 psi
Hardness (T81) 88 HB 88 HB
Tensile strength (T6, T651) 220 MPa 31900 psi
Yield strength (T6, T651) 195 MPa 28300 psi
Elongation (T6, T651) 15 % 15 %
Shear strength (T6, T651) 135 MPa 19600 psi
Fatigue strength (T6, T651) 69 MPa 10000 psi
Hardness (T6, T651) 90 HB 90 HB
Solution temperature 510 ºC 950 ºF
Aging temperature 160 ºC 320 ºF