Cast aluminum alloy 413.0

(submitted by the website administration)

Cast aluminum alloy 413.0
Chemical composition: Si=12%, Al balance, die casting
Property Value in metric unit Value in US unit
Density 2.66 *10³ kg/m³ 166 lb/ft³
Modulus of elasticity 71 GPa 10300 ksi
Thermal expansion (20 ºC) 20.4*10-6 ºCˉ¹ 11.3*10-6 in/(in* ºF)
Specific heat capacity 963 J/(kg*K) 0.230 BTU/(lb*ºF)
Thermal conductivity 121 W/(m*K) 840 BTU*in/(hr*ft²*ºF)
Electric resistivity 4.4*10-8 Ohm*m 4.4*10-6 Ohm*cm
Heat of fusion 3.89*105 J/kg 167 BTU/lb
Liquidus temperature 582 ºC 1080 ºF
Solidus temperature 574 ºC 1065 ºF
Tensile strength (F) 265 MPa 38440 psi
Yield strength (F) 140 MPa 20300 psi
Elongation (F) 2 % 2 %
Shear strength (F) 170 MPa 24700 psi
Fatigue strength (F) 130 MPa 18900 psi
Hardness (F) , range 30-60 HB 30-60 HB

Related internal links

Related external links

cast_aluminum_alloy_413.0.txt · Last modified: 2012/06/02 by dmitri_kopeliovich
Promote in SubsTech       Creative Commons License Except where otherwise noted, this work is licensed under a Creative Commons Attribution-Noncommercial-Share Alike 3.0 License