Wrought aluminum-manganese alloy 3005

(submitted by the website administration)

Wrought aluminum-manganese alloy 3005
Chemical composition: Mn=1.25%, Mg=0.4%, Al balance
Property Value in metric unit Value in US unit
Density 2.73 *10³ kg/m³ 170 lb/ft³
Modulus of elasticity 69 GPa 10000 ksi
Thermal expansion (20 ºC) 23.9*10-6 ºCˉ¹ 13.3*10-6 in/(in* ºF)
Specific heat capacity 890 J/(kg*K) 0.213 BTU/(lb*ºF)
Thermal conductivity 160 W/(m*K) 1110 BTU*in/(hr*ft²*ºF)
Electric resistivity 4.0*10-8 Ohm*m 4.0*10-6 Ohm*cm
Tensile strength (annealed) 130 MPa 18900 psi
Yield strength (annealed) 55 MPa 8000 psi
Elongation (annealed) 25 % 25 %
Shear strength (annealed) 83 MPa 12000 psi
Hardness (annealed) 35 HB 35 HB
Tensile strength (H18) 240 MPa 34800 psi
Yield strength (H18) 225 MPa 32600 psi
Elongation (H18) 4 % 4 %
Shear strength (H18) 146 MPa 21200 psi
Hardness (H18) 65 HB 65 HB
Annealing temperature 413 ºC 775 ºF