Wrought copper C10100 (Oxygen-Free Electronic Copper)

(submitted by the website administration)

Wrought copper C10100 (Oxygen-Free Electronic Copper)
Chemical composition: Cu = 99.99% min
Property Value in metric unit Value in US unit
Density 8.94 *10³ kg/m³ 558 lb/ft³
Modulus of elasticity 117 GPa 17000 ksi
Thermal expansion (20 ºC) 16.9*10-6 ºCˉ¹ 9.4*10-6 in/(in* ºF)
Specific heat capacity 394 J/(kg*K) 0.092 BTU/(lb*ºF)
Thermal conductivity 391 W/(m*K) 2712 BTU*in/(hr*ft²*ºF)
Electric resistivity 1.71*10-8 Ohm*m 1.71*10-6 Ohm*cm
Tensile strength (as fabricat.) 221 MPa 32000 psi
Yield strength (as fabricated) 69 MPa 10000 psi
Elongation (as fabricated) 55 % 55 %
Shear strength (as fabricated) 152 MPa 22000 psi
Hardness (as fabricated) 40 RF 40 RF
Tensile strength (cold work) 331 MPa 48000 psi
Yield strength (cold work) 303 MPa 44000 psi
Elongation (cold work) 16 % 16 %
Shear strength (cold work) 186 MPa 27000 psi
Fatigue strength (cold work) 117 MPa 17000 psi
Hardness (cold work) 47 RB 47 RB
Annealing temperature 425-650 ºC 800-1200 ºF
Liquidus temperature 1083 ºC 1981 ºF
Solidus temperature 1083 ºC 1981 ºF