Wrought aluminum alloy 1100

(submitted by the website administration)

Wrought aluminum alloy 1100
Chemical composition: Si + Fe =0.95% , Cu=0.12%, Al=99.0% min
Property Value in metric unit Value in US unit
Density 2.71 *10³ kg/m³ 169 lb/ft³
Modulus of elasticity 69 GPa 10000 ksi
Thermal expansion (20 ºC) 23.6*10-6 ºCˉ¹ 13.1*10-6 in/(in* ºF)
Specific heat capacity 904 J/(kg*K) 0.216 BTU/(lb*ºF)
Thermal conductivity 222 W/(m*K) 1540 BTU*in/(hr*ft²*ºF)
Electric resistivity 2.99*10-8 Ohm*m 2.99*10-6 Ohm*cm
Tensile strength (annealed) 90 MPa 13000 psi
Yield strength (annealed) 34 MPa 5000 psi
Elongation (annealed) 35 % 35 %
Shear strength (annealed) 62 MPa 9000 psi
Fatigue strength (annealed) 34 MPa 5000 psi
Hardness (annealed) 23 HB 23 HB
Tensile strength (H16) 145 MPa 21000 psi
Yield strength (H16) 138 MPa 20000 psi
Elongation (H16) 6 % 6 %
Shear strength (H16) 83 MPa 12000 psi
Fatigue strength (H16) 62 MPa 9000 psi
Hardness (H16) 38 HB 38 HB
Annealing temperature 343 ºC 650 ºF