Wrought aluminum-magnesium alloy 5052
Chemical composition: Mg=2.5%, Cr=0.25%, Al balance
Property Value in metric unit Value in US unit
Density 2.68 *10³ kg/m³ 167 lb/ft³
Modulus of elasticity 70 GPa 10200 ksi
Thermal expansion (20 ºC) 23.8*10-6 ºCˉ¹ 13.2*10-6 in/(in* ºF)
Specific heat capacity 880 J/(kg*K) 0.210 BTU/(lb*ºF)
Thermal conductivity 138 W/(m*K) 960 BTU*in/(hr*ft²*ºF)
Electric resistivity 4.99*10-8 Ohm*m 4.99*10-6 Ohm*cm
Tensile strength (annealed) 193 MPa 28000 psi
Yield strength (annealed) 90 MPa 13000 psi
Elongation (annealed) 25 % 25 %
Shear strength (annealed) 124 MPa 18000 psi
Fatigue strength (annealed) 110 MPa 16000 psi
Hardness (annealed) 47 HB 47 HB
Tensile strength (H38) 290 MPa 42000 psi
Yield strength (H38) 255 MPa 37000 psi
Elongation (H38) 7 % 7 %
Shear strength (H38) 165 MPa 24000 psi
Fatigue strength (H38) 138 MPa 20000 psi
Hardness (H38) 77 HB 77 HB
Annealing temperature 343 ºC 650 ºF