Wrought aluminum-magnesium alloy 5005
Chemical composition: Mg=0.80%, Al balance
Property Value in metric unit Value in US unit
Density 2.70 *10³ kg/m³ 169 lb/ft³
Modulus of elasticity 69 GPa 10000 ksi
Thermal expansion (20 ºC) 23.8*10-6 ºCˉ¹ 13.2*10-6 in/(in* ºF)
Specific heat capacity 900 J/(kg*K) 0.215 BTU/(lb*ºF)
Thermal conductivity 200 W/(m*K) 1390 BTU*in/(hr*ft²*ºF)
Electric resistivity 3.32*10-8 Ohm*m 3.32*10-6 Ohm*cm
Tensile strength (annealed) 124 MPa 18000 psi
Yield strength (annealed) 41 MPa 6000 psi
Elongation (annealed) 25 % 25 %
Shear strength (annealed) 76 MPa 11000 psi
Hardness (annealed) 28 HB 28 HB
Tensile strength (H38) 200 MPa 29000 psi
Yield strength (H38) 186 MPa 27000 psi
Elongation (H38) 5 % 5 %
Shear strength (H38) 110 MPa 16000 psi
Hardness (H38) 51 HB 51 HB
Annealing temperature 343 ºC 650 ºF