Wrought aluminum-copper alloy 2017

(submitted by the website administration)

Wrought aluminum alloy 2017
Chemical composition: Si=0.50%,Cu=4.0%, Mn=0.70%, Mg = 0.60%, Al balance
Property Value in metric unit Value in US unit
Density 2.79 *10³ kg/m³ 174 lb/ft³
Modulus of elasticity 72 GPa 10500 ksi
Thermal expansion (20 ºC) 23.6*10-6 ºCˉ¹ 13.1*10-6 in/(in* ºF)
Specific heat capacity 880 J/(kg*K) 0.21 BTU/(lb*ºF)
Thermal conductivity 193 W/(m*K) 1340 BTU*in/(hr*ft²*ºF)
Electric resistivity 3.49*10-8 Ohm*m 3.49*10-6 Ohm*cm
Tensile strength (annealed) 179 MPa 26000 psi
Yield strength (annealed) 69 MPa 10000 psi
Elongation (annealed) 22 % 22 %
Shear strength (annealed) 124 MPa 18000 psi
Fatigue strength (annealed) 90 MPa 13000 psi
Hardness (annealed) 45 HB 45 HB
Tensile strength (T651) 427 MPa 62000 psi
Yield strength (T651) 28 MPa 40000 psi
Elongation (T651) 22 % 22 %
Shear strength (T651) 262 MPa 38000 psi
Fatigue strength (T651) 124 MPa 18000 psi
Hardness (T651) 105 HB 105 HB
Annealing temperature 413 ºC 775 ºF
Solution temperature 505 ºC 940 ºF
Aging temperature 22 ºC 72 ºF