to Sintered aluminum alloys
to Properties of aluminum alloys

Sintered aluminum alloy B

(submitted by the website administration)

Sintered aluminum alloy B
Chemical composition: Si=0.6%, Cu=4.4%, Mg=0.5%, Al+Al2O3 balance
Property Value in metric unit Value in US unit
Density 90% of theoretical density
Modulus of elasticity 61 GPa 8800 ksi
Thermal conductivity 135 W/(m*K) 949 BTU*in/(hr*ft²*ºF)
Electric resistivity 4.9*10-8 Ohm*m 4.9*10-6 Ohm*cm
Tensile strength (T1) 201 MPa 29200 psi
Yield strength (T1) 170 MPa 24600 psi
Elongation (T1) 5 % 3 %
Tensile strength (T4) 245 MPa 35600 psi
Yield strength (T4) 205 MPa 29800 psi
Elongation (T4) 3.5 % 3.5 %
Shear strength (T4) 200 MPa 29000 psi
Compressive strength (T4) 179 MPa 26000 psi
Tensile strength (T6) 323 MPa 46800 psi
Yield strength (T6) 322 MPa 46700 psi
Elongation (T6) 0.5 % 0.5 %
Shear strength (T6) 179 MPa 26000 psi
Compressive strength (T6) 205 MPa 29700 psi

Related internal links

Related external links

sintered_aluminum_alloy_b.txt · Last modified: 2012/06/02 by dmitri_kopeliovich
Promote in SubsTech       Creative Commons License Except where otherwise noted, this work is licensed under a Creative Commons Attribution-Noncommercial-Share Alike 3.0 License