Silicate ceramics

Dr. Dmitri Kopeliovich

Silicates are materials composed generally of silicon and oxygen.

The following groups of materials relate silicate ceramics:

Technical Porcelain

Technical Porcelain generally consists of silica (SiO2) and alumina (Al2O3). The natural ingredients of these components are quartz, feldspar, soapstone and clay (kaolin).

Depending on the proportion of silica and alumina in material composition two types of porcelain may be prepared: quartz porcelain or alumina porcelain.

Alumina porcelain contains higher amount of more expensive alumina and possesses higher mechanical strength, than silica porcelain.

The following characteristics are typical for Technical Porcelain:

Technical porcelain is generally used in electrical engineering as a good insulator.

to top

Magnesium Silicates

Magnesium Silicates (Steatite and Cordierite) consist of silica (SiO2), magnesia (MgO) and some alumina (Al2O3).

The natural ingredients of Magnesium Silicates are soapstone, clay, corundum, mullite.

The process of steatite ceramic preparation:

  • Soapstone (talc) as a basic component + at least 10% of clay + fluxes (barium carbonate, BaO, CaO). Some SiO2 may be added for better firing. Type of the flux determines the electrical properties (work frequency) of the steatite ceramic.
  • The raw materials are wet milled to fine particles and mixed to form a slurry. The slurry is then either extruded or spraydried to spherical granules and pressed.
  • The firing temperature is 2460-2480F (1350-1360C). Strict temperature control is important.


The following characteristics are typical for Steatite:

  • High mechanical strength;
  • Good dielectric properties;
  • Very low loss factor;

Steatite is used in heat engineering and in electrical engineering for manufacturing sockets, control housings, insulating beads, low-voltage power fuses and base plates

The following characteristics are typical for Cordierite:

Cordierite is used mostly in heat engineering for manufacturing supports of heating elements, parts of water heaters, pipes of heating element, gas heater inserts, spark protectors and catalyst carriers in automobiles.

to top

Mullite Ceramics

Mullite Ceramics consist of mullite (3Al2O3*2SiO2), alumina (Al2O3) and glass (SiO2).

Sintered Mullite Ceramics have porosity up to 10%, which may be considerably reduced by increasing the content of glass phase above 10%.

The following characteristics are typical for Mullite Ceramics:

  • High strength;
  • High thermal shock resistance;
  • Relatively low thermal expansion;

Mullite Ceramics are used for manufacturing high temperature parts, kiln furniture, slide gates, ladles for molten metal, protection tubes for thermocouples, glass industry refractories.

to top

Properties of some silicate ceramics

Related internal links

silicate_ceramics.txt · Last modified: 2023/12/13 by dmitri_kopeliovich