Fluxes for melting aluminum

Dr. Dmitri Kopeliovich

Fluxes for melting aluminum are solid substances (commonly mixtures of chloride and fluoride salts) used in aluminum foundries in order to reduce the melt oxidation, minimize penetration of the atmospheric Hydrogen, absorb non-metallic inclusions suspended in the melt, keep the furnace/ladle wall clean from the built up oxides, decrease the content of aluminum entrapped in the dross, remove hydrogen dissolved in the melt, provide aluminum grain refining during Solidification, modify silicon inclusions in silicon containing alloys, oxidize excessive magnesium.

Common practice of flux introduction is manual application.
Most of the fluxes are applied on the melt surface and stirred into the melt. Some of the fluxes (degassing, grain refining) are plunged to the bottom by a clean preheated perforated bell.

Fluxes may also be introduced into the melt by injection in form of a powder in an inert gas (Argon or Nitrogen) stream.
The simplest flux injection technique is a lance immersed into the melt.
The most effective flux introduction method is injection by rotary degasser.

Classification of fluxes for melting aluminum

Cover fluxes

Melting point of a cover flux is lower than that of aluminum. Cover flux is applied on the surface of molten aluminum where it melts forming a continuous layer protecting the liquid metal from oxidation and absorption of atmospheric hydrogen. Cover fluxes are composed of a mixture of NaCl and KCl and may also contain some additions of CaCl2, CaF2 or KF. Fluorides (CaF2, KF) provide further decrease of the flux melting point and improve its cleaning ability. The disadvantage of fluoride containing fluxes is harmful fumes released by the flux at work temperature. Sodium free cover fluxes are used for melting hyper-eutectic aluminum-silicon alloys (alloys containing above 12.6% of Si). Hyper-eutectic alloys are modified by phosphorus, additions of which cause refining of the primary crystals of silicon. Sodium reduce the refining effect of phosphorus in such alloys.

to top

Drossing fluxes

Drossing fluxes promote separation of molten aluminum entrapped in the dross (sometimes up to 80%). Besides chlorides and fluorides drossing fluxes contain oxidizing component (KNO3) reacting exothermically with aluminum when heated. Heat generated by drossing flux improves wettability and fluidity of the entrapped aluminum, drops of which coalescence and flow down to the melt. The dross treated by the drossing flux is powdery and dry. It is easily removed from the furnace. Drossing fluxes helps to reduce losses of aluminum, which makes it very economically effective particularly in remelting aluminum scrap (chips, turnings etc.).

to top

Cleaning fluxes

Cleaning fluxes remove oxides suspended in the melt. Similarly to the Drossing fluxes a cleaning flux is composed of mixture of chlorides, fluorides and an oxidizing agent. Cleaning fluxes generate less heat therefore their aluminum separation effect is lower. However they possess better ability to absorb oxides inclusions from the melt.

to top

Wall cleaning fluxes

Wall cleaning fluxes soften oxides built up on the furnace walls. Wall cleaning fluxes contain double fluorides (Na2SiF6, Na2AlF6) and an oxidizing agent. The oxidizing agent reacts with aluminum generating heat, which promotes penetration of fluorides into the built up oxides softening them. The softened oxides are easily scrapped from the wall by the furnace operator.

to top

Degassing fluxes

Fluxes composed of chlorine and fluorine containing salts are used for degassing molten aluminum alloys. Degassing fluxes are commonly shaped in form of tablets. Degassing operation starts when a flux tablet is plunged by a clean preheated perforated bell to the furnace bottom. The flux components react with aluminum forming gaseous compounds (aluminum chloride, aluminum fluoride). The gas is bubbling and rising through the melt. Partial pressure of hydrogen in the formed bubbles is very low therefore it diffuses from the molten aluminum into the bubbles. The bubbles escape from the melt and the gas is then removed by the exhausting system. The process continues until bubbling ceases. Degassing flux may also be introduced by an injection method. In this case the inert gas serves as carrier for granulated flux. Besides the degassing effect the degassing treatment allows to remove non-metallic inclusions suspended in the melt (cleaning effect).

to top

Grain refiners

Grain refining fluxes composed of salts containing titanium and boron (K2TiF6 and KBF4). The fluxes cause formation of numerous nuclei of TiAl3 TiB2 when aluminum melt cools down. Aluminum grains start solidification on the nuclei surface. The average solid grain size is determined by the concentration of the nuclei in the melt before solidification. Fine grain structure is characterized by better fluidity during solidification, low Microsegregation of impurities, low shrinkage porosity. Alternative method of aluminum grain refining is introduction of master alloys containing titanium and boron (eg. Al-5%Ti-1%B).

to top

Silicon modifiers

hypo-eutectic and eutectic aluminum-silicon alloys are modified by fluxes containing sodium fluoride. Minor amount of sodium dissolved in the alloys refine the silicon structure resulting in improvement of mechanical properties (Fracture toughness#Toughness, ductility). Hypo-eutectic and eutectic aluminum-silicon alloys are also modified by introduction of metallic sodium or strontium.

to top

Demagging fluxes

Demagging fluxes are used when the melt contains excessive amount of magnesium. The flux helps to reduce the magnesium content by burning (oxidizing) it from the melt. Alternative demagging method is oxidizing the excessive magnesium by gaseous chlorine.

to top