Cast copper alloy C95500 (Aluminum Bronze)
Chemical composition: Al=11.0%, Fe=4.0%, Ni=4.3%, Cu=81.7%
Property Value in metric unit Value in US unit
Density 7.53 *10³ kg/m³ 470 lb/ft³
Modulus of elasticity 110 GPa 16000 ksi
Thermal expansion (20 ºC) 16.2*10-6 ºCˉ¹ 9.0*10-6 in/(in* ºF)
Specific heat capacity 419 J/(kg*K) 0.10 BTU/(lb*ºF)
Thermal conductivity 41.9 W/(m*K) 290 BTU*in/(hr*ft²*ºF)
Electric resistivity 20.4*10-8 Ohm*m 20.4*10-6 Ohm*cm
Tensile strength (sand cast) 689 MPa 100000 psi
Yield strength (sand cast) 303 MPa 44000 psi
Elongation (sand cast) 12 % 12 %
Shear strength (sand cast) 331 MPa 48000 psi
Fatigue strength (sand cast) 214 MPa 31000 psi
Hardness (sand cast) 195 HB(3000) 195 HB(3000)
Tensile strength (sand cast and quenched) 827 MPa 120000 psi
Yield strength (sand castand quenched) 469 MPa 68000 psi
Elongation (sand castand quenched) 10 % 10 %
Shear strength (sand castand quenched) 483 MPa 70000 psi
Fatigue strength (sand cast and quenched) 262 MPa 38000 psi
Hardness (sand castand quenched) 230 RB 230 RB
Liquidus temperature 1054 ºC 1930 ºF
Solidus temperature 1038 ºC 1900 ºF