Cast aluminum alloy 852.0

(submitted by the website administration)

Cast aluminum alloy 852.0
Chemical composition: Cu=2%, Mg=0.75%, Ni=1.2%, Sn=6.25%, Al balance, die casting
Property Value in metric unit Value in US unit
Density 2.88 *10³ kg/m³ 180 lb/ft³
Modulus of elasticity 71 GPa 10300 ksi
Thermal expansion (20 ºC) 23.2*10-6 ºCˉ¹ 12.9*10-6 in/(in* ºF)
Specific heat capacity 963 J/(kg*K) 0.230 BTU/(lb*ºF)
Thermal conductivity 172 W/(m*K) 1190 BTU*in/(hr*ft²*ºF)
Electric resistivity 3.8*10-8 Ohm*m 3.8*10-6 Ohm*cm
Heat of fusion 3.89*105 J/kg 167 BTU/lb
Liquidus temperature 635 ºC 1175 ºF
Solidus temperature 204 ºC 400 ºF
Tensile strength (F), min 186 MPa 27000 psi
Elongation (F), min 3 % 3 %
Shear strength (F) 115 MPa 16700 psi
Hardness (F) , range 55-85 HB 55-85 HB

Related internal links

Related external links

cast_aluminum_alloy_852.0.txt · Last modified: 2012/06/02 by dmitri_kopeliovich
Promote in SubsTech       Creative Commons License Except where otherwise noted, this work is licensed under a Creative Commons Attribution-Noncommercial-Share Alike 3.0 License