Cast aluminum alloy 713.0

(submitted by the website administration)

Cast aluminum alloy 713.0
Chemical composition: Cu=0.7%, Mg=0.35%, Zn=7.5%, Al balance, sand casting
Property Value in metric unit Value in US unit
Density 2.81 *10³ kg/m³ 175 lb/ft³
Modulus of elasticity 71 GPa 10300 ksi
Thermal expansion (20 ºC) 24.1*10-6 ºCˉ¹ 13.4*10-6 in/(in* ºF)
Specific heat capacity 963 J/(kg*K) 0.230 BTU/(lb*ºF)
Thermal conductivity 121 W/(m*K) 841 BTU*in/(hr*ft²*ºF)
Electric resistivity 5.7*10-8 Ohm*m 5.7*10-6 Ohm*cm
Heat of fusion 3.89*105 J/kg 167 BTU/lb
Liquidus temperature 638 ºC 1180 ºF
Solidus temperature 593 ºC 1100 ºF
Tensile strength (F) ,min. 221 MPa 32000 psi
Yield strength (F) ,min. 152 MPa 22000 psi
Elongation (F) ,min. 3 % 3 %
Shear strength (F) 180 MPa 26100 psi
Fatigue strength (F) 60 MPa 8700 psi
Hardness (F) , range 60-90 HB 60-90 HB
Tensile strength (T5) 235 MPa 34100 psi
Yield strength (T5) 175 MPa 25400 psi
Elongation (T5) 4 % 4 %

Related internal links

Related external links

cast_aluminum_alloy_713.0.txt · Last modified: 2012/06/02 by dmitri_kopeliovich
Promote in SubsTech       Creative Commons License Except where otherwise noted, this work is licensed under a Creative Commons Attribution-Noncommercial-Share Alike 3.0 License